電工鋼硅鋼片Ultra-thin series: B15AHT1000, B15AHT1200, B15AT1000, B15AT1200B15AT1500, B15AT1550, B20AHT1000, B20AHT1200, B20AT1000, B20AT1200, B20AT1500, 20WTG1200, 20WTG1500 20WTG1550 B25AHV1200 B25AHV1300, B27AHV1400, B27AV1400, B30AHV1500 B30AHV1400, B35AV1700 B35AV1800High performance series: B35AH300, B50AH300, 50AH470, 50AH600, 50AH800, B50AH470, B50AH600, B50AH800, B50AR300, B50AR600, B50AR500, B50AR350, B20AT15000.35 series: B35A200, B35A210, B35A230, B35A250, B35A270,B35A300, B35A360, B35A440, B35A550, B35AH300, B35AR300, B35AY-10.5 series: B50A250, B50A270, B50A290, B50A310, B50A350, B50A400, B50A470, B50A600, B50A700, B50A800, B50A1000, B50A13000.65 series: B65A470, B65A530, B50A600B65A700, B65A800 B65A1000, B65A1300Super thick Series: 70WK340, 75WK400, 80WK420, 85WK450, 10W800 WFC-100A, silicon steel sheet performance: A low iron loss. As an important indicator of quality, each country divides the grade by the iron loss value. The lower the iron loss, the higher the grade and the higher the quality.B. High magnetic induction strength. Under the same magnetic field, the silicon steel sheet with high magnetic sensitivity can be obtained. The volume and weight of the iron core of the motor or transformer made by it are relatively small, which can save silicon steel sheet, copper wire and insulating materials, etc.C. High stacking coefficient. The surface of the silicon steel sheet is smooth, flat and uniform in thickness, which improves the stacking coefficient of the iron core.D. Good punching property. This is more important for manufacturing small and micro motor iron cores.E. The surface has good adhesion and weldability to the insulating film.

電工鋼硅鋼片涂層為鉻酸鹽為主的無機成分混合物，添加有少量有機成分，以提高鋼帶的沖片性能。涂層具有一定的層間電阻，在中性氣氛或弱還原性爐子氣氛中，可承受的應力退火溫度一般可達800℃，在退火時，層間電阻會有一些降低。涂層能承受 300-550℃的涂層燒除處理，可用于重建電機定子時，去除電機定子繞組的絕緣層，也可用于風冷式或油浸式。涂層基本情況和 A 涂層類似，膜厚增加，絕緣性更好，耐蝕性更好，沖片性也更好，焊接性略差。