電工鋼硅鋼片5 剪切適應性鋼帶應便于進行剪切或沖壓 ,以保證在任何位置將鋼帶剪切成通常的形狀。7 技術要求7.1 磁性能在 6.3 條件下提供的產品的磁性能應符合表 3 和表 4 的規(guī)定。時效后的磁性能要求，由供需雙方在訂貨時協(xié)商，并在合同中注明。表 3 普通型 A、江蘇鎮(zhèn)江本地應力退火型 AR、江蘇鎮(zhèn)江本地型 AH 產品磁性能和技術特性類型 牌號公稱厚度mm 比總損耗名義值P1.5/50 W/kg 比總損耗P1.5/50 W/kg小磁極化強度J5000a T比總損耗各向異性T1.5/50b ％小疊裝系數小彎曲次數約定密度kg/dm3普通型B35A2000.352.00 2.00 1.62 ±170.952 7.60B35A210 2.10 2.10 1.62 ±17 2 7.60B35A230 2.30 2.28 1.64 ±17 2 7.60B35A250 2.50 2.45 1.64 ±17 2 7.60B35A270 2.70 2.65 1.64 ±17 2 7.65B35A300 3.00 2.90 1.64 ±17 3 7.65B35A360 3.60 3.20 1.65 ±17 3 7.65B35A440 4.40 3.40 1.67 ±17 3 7.70B50A2300.502.30 2.30 1.64 ±170.972 7.60B50A250 2.50 2.48 1.64 ±17 2 7.60B50A270 2.70 2.65 1.64 ±17 2 7.60B50A290 2.90 2.85 1.64 ±17 2 7.60B50A310 3.10 3.00 1.65 ±14 3 7.65B50A350 3.50 3.20 1.65 ±12 5 7.65B50A400 4.00 3.30 1.66 ±12 5 7.70B50A470 4.70 4.20 1.67 ±10 10 7.70B50A600 6.00 4.70 1.68 ±10 10 7.75B50A700 7.00 5.50 1.71 ±10 10 7.80B50A800 8.00 5.80 1.71 ±10 10 7.80B50A1000 10.00 6.00 1.74 ±8 10 7.85B50A1300 13.00 7.00 1.74 ±8 10 7.85B65A3100.653.10 3.05 1.64 ±150.972 7.60B65A350 3.50 3.45 1.65 ±14 2 7.60B65A400 4.00 3.95 1.66 ±14 2 7.65B65A470 4.70 4.60 1.67 ±12 5 7.65B65A530 5.30 5.20 1.68 ±12 10 7.70B65A600 6.00 5.90 1.68 ±10 10 7.75B65A700 7.00 6.90 1.69 ±10 10 7.75B65A800 8.00 7.90 1.71 ±10 10 7.80B65A1000 10.00 9.90 1.71 ±10 10 7.80B65A1300 13.00 12.90 1.72 ±8 10 7.

電工鋼硅鋼片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example: